7Cr7Mo3V2Si鋼適宜制造承受高負荷的冷擠、冷鐓、冷沖模具
|
C |
Cr |
Mo |
V |
Si |
Mn |
P |
S |
|
0.70~0.80 |
6.50~7.50 |
2.00~3.0 |
1.70~2.20 |
0.70~1.20 |
≤0.50 |
≤0.030 |
≤0.030 |
7Cr7Mo3V2Si鋼的熱加工條件
|
加熱溫度/℃ |
始鍛溫度/℃ |
終鍛溫度/℃ |
冷 卻 |
|
1120~1130 |
1100 |
≥850 |
緩(huan)冷(leng)（坑冷(leng)或砂冷(leng)） |